Three Translucency Heat-treatment of Two Ceramic CAD Milling Blocks and their Effect on Leakage and Film Thickness
Main Article Content
Abstract
This study aims to evaluate and compareleakage and film thickness when applying three translucency heat-treatment to two CAD Milling blocks(Emax CAD and Amber Mill) considering temperature and holding time for translucency heat-treatment.120 cemented laminate veneers were randomly divided into two groups, Group 1: (Amber Mill, N=60), and Group 2: (Emax CAD, N=60). Then, they were divided into 3 subgroups, based on thermal temperature. the measurements of film thickness and leakage were applied.a two-way ANOVA was used. Student's t-test was used to compare between two materials.It has been found that the firing cycles and translucency levels had a significant effect on both leakage and film thickness.The degree of translucency and direction of manufacturing during firings has direct effect on both film thickness and leakage. there is a direct relationship between increasing the degree of translucency of Amber Mill and leakage and film thickness.
Article Details

This work is licensed under a Creative Commons Attribution 4.0 International License.